Faktor Apa Yang Menghancurkan Kehalusan Badan Botol Pada Pembuatan Botol Kaca

Nov 17, 2022

Tinggalkan pesan

1. Ketika kaca kosong jatuh ke cetakan awal, ia tidak dapat memasuki cetakan awal secara akurat, dan gesekan dengan dinding cetakan terlalu besar, membentuk lipatan. Setelah ditiup, lipatan menyebar dan membesar, membentuk kerutan pada badan botol kaca.


2. Tanda gunting pada mesin pengumpan atas terlalu besar, dan tanda gunting muncul di badan beberapa botol kaca setelah dicetak.


1. When the glass blank falls into the initial mold, it cannot enter the initial mold accurately, and the friction with the mold wall is too large, forming creases. After blowing, the creases spread and enlarge, forming wrinkles on the glass bottle body. 2. The scissor mark of the upper feeding machine is too large, and the scissor mark appears on the body of some glass bottles after molding. 3. The material of the glass bottle initial mold and molding is poor, the density is not enough, and the oxidation is too fast after high temperature, forming small pits on the surface of the mold, resulting in the surface of the glass bottle being not smooth after molding. 4. The poor quality of glass bottle mold oil will cause insufficient lubrication of the mold, slow down the dripping speed of lubricating oil, and change the material shape too quickly. 5. The initial mold design is unreasonable, the mold cavity is large or small, and after the material drops into the forming mold, it is blown and diffused unevenly, which will cause spots on the body of the glass bottle. 6. The dropping speed of the machine is not uniform, and the improper adjustment of the tuyere will cause the temperature of the glass bottle initial mold and mold forming to be uncoordinated, and it is easy to create cold spots on the glass bottle body, which directly affects the finish. 7. If the glass material liquid in the kiln is not clean or the temperature of the material is not uniform, it will also cause bubbles, small particles, and small flakes to appear in the output glass bottles. 8. If the machine speed is too fast or slow, the glass bottle body will be uneven, and the bottle wall thickness will vary, resulting in mottling. The above are the factors that easily cause or damage the smoothness of the bottle body during the production of glass bottles.


3. Bahan cetakan dan cetakan awal botol kaca buruk, kerapatannya tidak cukup, dan oksidasi terlalu cepat setelah suhu tinggi, membentuk lubang kecil di permukaan cetakan, sehingga permukaan botol kaca menjadi tidak licin setelah dibentuk.


4. Kualitas minyak cetakan botol kaca yang buruk akan menyebabkan pelumasan cetakan yang tidak mencukupi, memperlambat kecepatan tetesan minyak pelumas, dan mengubah bentuk material terlalu cepat.


5. Desain cetakan awal tidak masuk akal, rongga cetakan besar atau kecil, dan setelah bahan jatuh ke dalam cetakan pembentuk, ditiup dan disebarkan secara tidak merata, yang akan menimbulkan bintik-bintik pada badan botol kaca.


1. When the glass blank falls into the initial mold, it cannot enter the initial mold accurately, and the friction with the mold wall is too large, forming creases. After blowing, the creases spread and enlarge, forming wrinkles on the glass bottle body. 2. The scissor mark of the upper feeding machine is too large, and the scissor mark appears on the body of some glass bottles after molding. 3. The material of the glass bottle initial mold and molding is poor, the density is not enough, and the oxidation is too fast after high temperature, forming small pits on the surface of the mold, resulting in the surface of the glass bottle being not smooth after molding. 4. The poor quality of glass bottle mold oil will cause insufficient lubrication of the mold, slow down the dripping speed of lubricating oil, and change the material shape too quickly. 5. The initial mold design is unreasonable, the mold cavity is large or small, and after the material drops into the forming mold, it is blown and diffused unevenly, which will cause spots on the body of the glass bottle. 6. The dropping speed of the machine is not uniform, and the improper adjustment of the tuyere will cause the temperature of the glass bottle initial mold and mold forming to be uncoordinated, and it is easy to create cold spots on the glass bottle body, which directly affects the finish. 7. If the glass material liquid in the kiln is not clean or the temperature of the material is not uniform, it will also cause bubbles, small particles, and small flakes to appear in the output glass bottles. 8. If the machine speed is too fast or slow, the glass bottle body will be uneven, and the bottle wall thickness will vary, resulting in mottling. The above are the factors that easily cause or damage the smoothness of the bottle body during the production of glass bottles.


6. Kecepatan menjatuhkan mesin tidak seragam, dan penyesuaian tuyere yang tidak tepat akan menyebabkan suhu cetakan awal botol kaca dan pembentukan cetakan menjadi tidak terkoordinasi, dan mudah untuk membuat bintik-bintik dingin pada badan botol kaca, yang secara langsung mempengaruhi hasil akhir.


7. Jika cairan bahan kaca di dalam kiln tidak bersih atau suhu bahan tidak seragam, juga akan menyebabkan gelembung, partikel kecil, dan serpihan kecil muncul di botol kaca keluaran.


8. Jika kecepatan mesin terlalu cepat atau lambat, badan botol kaca akan menjadi tidak rata, dan ketebalan dinding botol akan bervariasi, sehingga menimbulkan bintik-bintik.


Di atas adalah faktor-faktor yang dengan mudah menyebabkan atau merusak kelancaran badan botol pada saat produksi botol kaca.